Elastollan TPU 1190A10 德国巴斯夫 其它用途:特性:密度: 1.13 g cm3  断裂伸长率: 580 %  弯曲模量: 44.8 MPa  硬度: 91

一.聚酯型TPU与聚醚型的比较

表34给出5种牌号TPU弹性体的硬度与密度的比较。聚酯型TPU硬度为62A～75D的密度在1.15～1.25g/cm3。这说明在同等体积时，聚醚型TPU的质量稍轻，而销售是以质量不是体积，所以在设计 、购买和生产时，要考虑这个重要的密度差别。

TPU弹性体的物理性能包括密度、线性膨胀系数、摩擦系数、气体扩散系数、传热系数、玻璃化转变温度、熔点、熔化热、比热容和特性粘度等。

1、密度

TPU的密度大约在1.10～1.25之间，在同等硬度时聚醚型TPU密度比聚酯型TPU低。TPU密度决定于软段种类、分子量、硬段或软段含量以及TPU聚集态。这一部分讨论TPU与橡胶和塑料的比较、软段类型的影响、TPU分子量的影响、软段取代基的影响和硬段含量的影响。

（1）与橡胶和塑料的比较

TPU密度与橡胶和塑料的比较示于表33。由此可见TPU密度与其他橡胶和塑料无显著差异。

Physical Properties	Metric	English	Comments
Density	1.13 g/cc @Thickness 2.00 mm	0.0408 lb/in3 @Thickness 0.0787 in	molded plaque, cured 20 hr at 100°C; ASTM D792
Mechanical Properties	Metric	English	Comments
Hardness, Shore A	90 @Thickness 2.00 mm	90 @Thickness 0.0787 in	molded plaque, cured 20 hr at 100°C; ASTM D2240
Tensile Strength, Ultimate	55.0 MPa @Thickness 2.00 mm	7980 psi @Thickness 0.0787 in	molded plaque, cured 20 hr at 100°C; ASTM D412
Tensile Strength, Yield	9.00 MPa @Strain 100 %	1310 psi @Strain 100 %	ASTM D-412
	25.0 MPa @Strain 300 %	3630 psi @Strain 300 %	0.76 mm (0.030 in) extruded sheet; ASTM D-412
Elongation at Break	500 %	500 %	on 0.030 in extruded sheet; ASTM D-412
Flexural Modulus	0.0500 GPa @Thickness 2.00 mm	7.25 ksi @Thickness 0.0787 in	molded plaque, cured 20 hr at 100°C; ASTM D790
Tear Strength	58.0 kN/m @Thickness 0.762 mm	331 pli @Thickness 0.0300 in	Split tear strength, extruded sheet; ASTM D-1938
Graves Tear Strength	114 kN/m @Thickness 0.762 mm	650 pli @Thickness 0.0300 in	extruded sheet; ASTM D624
Taber Abrasion, mg/1000 Cycles	30 @Thickness 2.00 mm	30 @Thickness 0.0787 in	H-18 wheel; ASTM D-1044; molded plaque, cured 20 hr at 100°C.
Compression Set	45 % @Temperature 70.0 °C	45 % @Temperature 158 °F	22 hr @ 70°C; ASTM D-395; 0.080 in molded plaque after curing 20 hrs at 100°C.
	25 % @Thickness 2.00 mm	25 % @Thickness 0.0787 in	22 hr at 23°C; molded plaque, cured 20 hr at 100°C.; ASTM D395
Tensile Set	32 %	32 %	at 200% elongation per ASTM D-412 is on 0.030 in extruded sheet.