赛诺硅酸锆珠(CZS):
        采用电解液中滴定成形，高温烧结定相的先进工艺制成。珠内由致密的硅酸锆微粒组成微观结构，拒绝了毛隙和空腔，避免了晶相和玻璃相的分离，比同类珠子有更大的密度和硬度，磨耗率是同类硅酸锆珠的1/2。中等的密度和硬度适合中低粘度浆料的分散和研磨，可匹配绝对部分的砂磨机，为通用型磨介。
氧化锆含量:  64%,                    氧化硅含量:  33%,
比            重:  4.2kg/dm3,        散            重:  2.6kg/L,
莫  氏  硬度:  7.3,                    维  氏  硬度:  1100kg/mm2,  
耐  压  强度:  1200N(2mm),      粒            径:  0.6-3.2mm,
吨    磨    耗:  0.05kg/吨,        包            装:  25kg/桶
CZS  zirconium  silicate  beads  are  shaped  in  electrolyte  solution  and  hardened  at  a  high  temperature  in  kilin.  Compared  to  the  other  zircon  beads  and  the  ATZ  beads,  they  have  homogenous  microstructure  and  no  air  pockets.  This  give  them  1/2  lower  beads  wear  than  the  others.  The  middle  density  and  high  crushing  strength  features  are  suitable  to  grinding  slurry  in  visicosity  from  low  to  middle  in  more  kinf  of  beads  mills.
ZrO2  %:  64  ,                                      SiO2  %:  33
Density:  4.2kg/dm3,                        Bulk  Density:  2.56kg/L
Hardness  Vickers:  1000kg/mm2,    Crushing  Strength:  1000N  (2mm),  
Sizes:  0.6-5.5mm  ,                          Packing:  25kg/bucket