耐诺陶瓷球(NanorAl)：
        采用煅烧超细的氧化铝粉为主要成份，干粉等静压成形和高温焙烧定相的工艺制成。具有高硬度和高比重的特性，适合大球磨机和振动磨对部分物料的分散和研磨。
氧化铝含量:  92.3%,              氧化硅含量:  4.3%,
比            重:  3.7kg/dm3,      散            重:  2.2kg/L,
莫  氏  硬度:  9,                      维  氏  硬度:  1300kg/mm2,
吸    水    率:  0.01%,              粒            径:  1-80mm,
颜            色:  白色,                包            装:  25kg/袋.      
NanorAl  alumina  balls  are  made  by  dry  isostatic  press  and  sintered  at  high  temperature  by  micro  fine  alumina  powder.  The  small  crystal    size  is  free  from  air  pockets  and  has  better  wear  resistance.  It  is  ideal  media  for  large  ball  mills.
Al2O3  %:  92.3  ,                        SiO2/MgO/CaO  %:  7
Density:  3.7kg/dm3,                Bulk  Density:  2.2kg/L,
Hardness  Vickers:  1300kg/mm2,  Crushing  Strength:  2000N,  
Sizes:  0.3-5.5mm  ,                  Packing:  25kg/bag