赛诺硅酸锆球(CZS-64B)：
        采用精选的硅酸锆粉经独特的成胚和成形工艺高温烧结而成，致密的微观结构尽量降低了剥皮和破碎的发生；低磨耗、中密度和高抗碎强度为球磨介质带来新的革命。为球石的理想代替品。
氧化锆含量:  62%,                    氧化硅含量:  35%,
比            重:  4.3kg/dm3,        散            重:  2.5kg/L,
莫  氏  硬度:  7.5,                    维  氏  硬度:  1100kg/mm2,  
粒            径:  3.0-13.0mm,      颜            色:  米白,                
包            装:  25kg/桶
Zirconium  Silicate  Balls  CZS-64B    are  shaped  with  granulating  and  compacting  press  method  and  sintered  at  high  temperature  in  a  kiln.  The  compacted  and  homogenous  microstructure  of  zirconium  silicate  to  form  a  tough  and  non  porous  woking  surface.  Due  to  the  lower  wear  rate,  middle  density  and  higher  toughness  strength,  it  is  suitable  to  millling  low  to  middle  density  slurries  which  refuse  the  alumina  contamination.        
ZrO2  %:  62  ,                              SiO2  %:  33
Density:  4.1kg/dm3,                Bulk  Density:  2.50kg/L
Hardness  Vickers:  1100kg/mm2
Toughness:  7Mpa.m1/2,            Sizes:  3-13mm