耐诺氧化锆球(NanorZr-95B):
        采用氧化钇作稳定，干粉等静压成形，烧结定相的工艺制成。PPM级的磨耗和优异的抗剪切性特别适合篮式砂磨机、立式搅拌磨、卧式滚动磨、振动磨等设备对拒绝污染的浆料和粉料的湿法和干法的超细分散和研磨。
氧化锆含量:  95%,                氧化钇含量:  5%,
比            重:  6.0kg/dm3,    散            重:  3.6kg/L,
莫  氏  硬度:  9,                    维  氏  硬度:  1300kg/mm2,
断  裂  韧性:  10Mpa.m1/2    弹  性  模量:  200Gpa,  
粒            径:  3-50mm,          颜            色:  奶白,
包            装:  25kg/桶.
NanorZr-95B  zirconiium  oxide  balls  are  manufactured  from  dry  Yttria  Stabilized  Zirconi  powder  by  high  compaction  press.  Then  was  sintered  at  a  high  temperature  to  form  a  Tetragonal  Zirconia  Polycrystal(Y-TZP)  microstructure.  The  highest  crushing  strength  and  fracture  toughness  was  considered  the  first  choice  of  grinding  media  to  mill  the  contamination-free  powder  or  slurry.  
ZrO2  %:  95  ,                              Y2O3  %:  5
Density:  6.0kg/dm3,                Hardness  Vickers:  1300kg/mm2
Toughness:  10Mpa.m1/2,          Crushing  Strength:  2300N  (2mm)
Sizes:  3-50mm  ,                        Packing:  25kg/bucket