耐诺滑石球(NanorMg)：  
        耐诺滑石球（NanorMg）采用高纯度、精细的滑石瓷粉经滚动和等静压成形，高温焙烧定相的工艺制成。均匀的微观结构保证了优良的耐磨性，适合对浅色低粘度物料的球磨。有球型和圆柱两种选择。
氧化硅含量:  62%,                        氧化镁含量:  27%,
比            重:  2.7kg/dm3,            散            重:  1.6kg/L,
莫  氏  硬度:  7.5,                        耐  压  强度:  650N(2mm),
颜            色:  白,                          粒            径:  3.0-40.0mm,  
包            装:  25kg/包
NanorMg  Steatile  Balls:
NanorMg  steatile  balls  are  manufactured  from  a  special  fine  clay  in  a  sinter  method.  The  homogeneous  magnesium  silicate  microstructure  results  in  perfect  wear-resistance.  It  is  used  for  grinding  slight  colour  and  low  viscosity  materials.There  are  two  tppe  shape:  ball  and  cylinder  for  selection.
SiO2  %:  62  ,                              MgO  %:  27
Density:  2.7kg/dm3,                Bulk  Density:  1.6kg/L            
Hardness  Mohs:  7.5,                Toughness:  7Mpa.m1/2,  
Sizea:  3-40mm,                          Packing：25kg/bag