耐诺玛瑙球(NanorAg):
        采用纯天然的进口玛瑙石经切割，打磨和抛光等工艺制成。具有结构致密，色泽通透，高弹性模量和优异的耐磨性。形状有球形、圆柱形和方形等。特别适合立式搅拌磨机、卧式滚动磨和振动磨对浅色物料的分散和研磨。
氧化硅含量:  94%,                          氧化镁/氧化钙含量:  6%,
比            重:  2.65kg/dm3,            散                          重:  1.6kg/L,
莫  氏  硬度:  7,                              弹      性      模      量:  63Gpa,  
粒            径:  3-40mm,                    颜                          色:    奶白或灰色,  
包            装:  25kg/桶.  
NanorAg  agate  ball  is  made  from  high  quality  natural  agate  stones.  The  complex  process  include  cutting,  abrading,  polishing  and  sieving.  There  are  3  types  of  shape:  ball,  cylinder  and  square.  Due  to  higher  density  and  better  chip  resistance  than  glass  balls,  they  can  be  used  in  the  vertical  stirring  ball  mills,  horizontal  rotary  ball  mills,  vibrational  mills  for  grinding  tiny  color  products.
SiO2  %:  94  ,                                                MgO/CaO  %:  6
Specific  Density:  2.65kg/dm3,              Bulk  Density:  1.58kg/L
Hardness  Mohs:  70Gpa,                              Elasticity  Modulus:  70Gpa  
Sizes:  3-40mm  ,                                          Packing:  25kg/bucket