型号：Cycoloy PC/ABS C6200
性能：阻燃级，阻燃PC/ABS 耐热级。
CYCOLOY? Resin C6200
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 阻燃PC/ABS C6200
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：SABIC
价格：面议
元/KG
供应地：广东省东莞市
产品型号：C6200
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
Property
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
680
kgf/cm2
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
50
%
ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span
1050
kgf/cm2
ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span
27400
kgf/cm2
ASTM D 790
IMPACT
Izod Impact, notched, 23°C
54
cm-kgf/cm
ASTM D 256
Instrumented Impact Energy @ peak, 23°C
622
cm-kgf
ASTM D 3763
Instrumented Impact Energy @ peak, -30
553
cm-kgf
ASTM D 3763
THERMAL
HDT, 1.82 MPa, 3.2mm, unannealed
87
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed
90
°C
ASTM D 648
Relative Temp Index, Elec
85
°C
UL 746B
Relative Temp Index, Mech w/impact
85
°C
UL 746B
Relative Temp Index, Mech w/o impact
85
°C
UL 746B
PHYSICAL
Specific Gravity
1.18
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Melt Flow Rate, 260°C/2.16 kgf
14.5
g/10 min
ASTM D 1238
Spiral Flow,260°C,10 ips,3.175 X 1524 mm
685.8
mm
-
ELECTRICAL
Arc Resistance, Tungsten {PLC}
6
PLC Code
ASTM D 495
Hot Wire Ignition {PLC)
2
PLC Code
UL 746A
High Voltage Arc Track Rate {PLC}
3
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
0
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
2
PLC Code
UL 746A
Volume Resistivity
>1.E+15
Ohm-cm
IEC 60093
Surface Resistivity, ROA
>1.E+15
Ohm
IEC 60093
Dielectric Strength, in oil, 0.8 mm
35
kV/mm
IEC 60243-1
Dielectric Strength, in oil, 1.6 mm
25
kV/mm
IEC 60243-1
Dielectric Strength, in oil, 3.2 mm
17
kV/mm
IEC 60243-1
Relative Permittivity, 1 MHz
2.7
-
IEC 60250
Dissipation Factor, 50/60 Hz
0.004
-
IEC 60250
Dissipation Factor, 1 MHz
0.008
-
IEC 60250
Relative Permittivity, 50/60 Hz
2.8
-
IEC 60250
FLAME CHARACTERISTICS
UL Recognized, 94HB Flame Class Rating (3)
0.71
mm
UL 94
UL Recognized, 94V-1 Flame Class Rating (3)
1.21
mm
UL 94
UL Recognized, 94V-0 Flame Class Rating (3)
1.47
mm
UL 94
UL Recognized, 94-5VA Rating (3)
3.4
mm
UL 94
UL Recognized, 94-5VB Rating (3)
2
mm
UL 94
Source GMD, last updated:2000/01/05
Processing
Injection Molding
Drying Temperature
80 - 90
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
245 - 275
°C
Nozzle Temperature
245 - 275
°C
Front - Zone 3 Temperature
245 - 275
°C
Middle - Zone 2 Temperature
220 - 275
°C
Rear - Zone 1 Temperature
220 - 255
°C
Mold Temperature
60 - 80
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
30 - 80
%
Vent Depth
0.038 - 0.076
mm