CYCOLOY? Resin C3650

Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according to DIN VDE 0472/815 for cable channels

Tensile Stress, yld, Type I, 50 mm/min

660

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

520

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

4.9

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

35

%

ASTM D 638

Tensile Modulus, 50 mm/min

29100

kgf/cm2

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

1030

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

27400

kgf/cm2

ASTM D 790

Tensile Stress, yield, 5 mm/min

55

MPa

ISO 527

Tensile Stress, break, 5 mm/min

50

MPa

ISO 527

Tensile Stress, yield, 50 mm/min

65

MPa

ISO 527

Tensile Stress, break, 50 mm/min

55

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

3

%

ISO 527

Tensile Strain, break, 5 mm/min

55

%

ISO 527

Tensile Strain, yield, 50 mm/min

4.5

%

ISO 527

Tensile Strain, break, 50 mm/min

>50

%

ISO 527

Tensile Modulus, 1 mm/min

2600

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

100

MPa

ISO 178

Flexural Modulus, 2 mm/min

2700

MPa

ISO 178

Hardness, H358/30

113

MPa

ISO 2039-1

Hardness, Rockwell R

124

-

ISO 2039-2

Izod Impact, notched, 23°C

70

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

662

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*4 +23°C

45

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*4 0°C

15

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*4 -30°C

13

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm

48

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm

13

kJ/m2

ISO 179/1eA

Vicat Softening Temp, Rate B/50

110

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed

100

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

88

°C

ASTM D 648

CTE, -40°C to 40°C, flow

7.2E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

7.2E-05

1/°C

ASTM E 831

Thermal Conductivity

0.2

W/m-°C

ISO 8302

CTE, 23°C to 60°C, flow

8.E-05

1/°C

ISO 11359-2

CTE, 23°C to 60°C, xflow

8.E-05

1/°C

ISO 11359-2

Vicat Softening Temp, Rate B/50

108

°C

ISO 306

Vicat Softening Temp, Rate B/120

110

°C

ISO 306

HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm

102

°C

ISO 75/Be

HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

91

°C

ISO 75/Ae

Relative Temp Index, Elec

60

°C

UL 746B

Relative Temp Index, Mech w/impact

60

°C

UL 746B

Relative Temp Index, Mech w/o impact

60

°C

UL 746B

Specific Gravity

1.2

-

ASTM D 792

Water Absorption, (23°C/sat)

0.6

%

ASTM D 570

Mold Shrinkage, flow, 3.2 mm (5)

0.4 - 0.6

%

SABIC Method

Melt Flow Rate, 260°C/5.0 kgf

8.5

g/10 min

ASTM D 1238

Density

1.18

g/cm3

ISO 1183

Melt Volume Rate, MVR at 260°C/5.0 kg

8

cm3/10 min

ISO 1133

Dissipation Factor, 50/60 Hz

0.006

-

ASTM D 150

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity, ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil, 0.8 mm

35

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 1.6 mm

25

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 3.2 mm

17

kV/mm

IEC 60243-1

Relative Permittivity, 1 MHz

2.7

-

IEC 60250

Dissipation Factor, 50/60 Hz

0.004

-

IEC 60250

Dissipation Factor, 1 MHz

0.006

-

IEC 60250

Comparative Tracking Index

600

V

IEC 60112

Relative Permittivity, 50/60 Hz

2.8

-

IEC 60250

UL Recognized, 94V-0 Flame Class Rating (3)

1.49

mm

UL 94

UL Recognized, 94-5VB Rating (3)

2.48

mm

UL 94

Oxygen Index (LOI)

37

%

ISO 4589

Source GMD, last updated:2001/05/26

Drying Temperature

80 - 90

°C

Drying Time

3 - 4

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0.04

%

Melt Temperature

245 - 275

°C

Nozzle Temperature

245 - 275

°C

Front - Zone 3 Temperature

245 - 275

°C

Middle - Zone 2 Temperature

220 - 265

°C

Rear - Zone 1 Temperature

220 - 255

°C

Mold Temperature

60 - 80

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

40 - 70

rpm

Shot to Cylinder Size

30 - 80

%

Vent Depth

0.038 - 0.076

mm

Drying Temperature

80 - 90

°C

Drying Time

2 - 4

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0 - 0.02

%

Melt Temperature (Parison)

225 - 250

°C

Barrel - Zone 1 Temperature

205 - 230

°C

Barrel - Zone 2 Temperature

215 - 245

°C

Barrel - Zone 3 Temperature

215 - 245

°C

Barrel - Zone 4 Temperature

220 - 250

°C

Adapter - Zone 5 Temperature

225 - 250

°C

Head - Zone 6 - Top Temperature

225 - 250

°C

Head - Zone 7 - Bottom Temperature

225 - 250

°C

Mold Temperature

65 - 90

°C

Die Temperature

240 - 250

°C

Drying Temperature

80 - 90

°C

Drying Time

2 - 4

hrs

Drying Time (Cumulative)

8

hrs

Minimum Moisture Content

0 - 0.02

%

Melt Temperature

225 - 270

°C

Barrel - Zone 1 Temperature

205 - 250

°C

Barrel - Zone 2 Temperature

215 - 260

°C

Barrel - Zone 3 Temperature

215 - 260

°C

Barrel - Zone 4 Temperature

225 - 270

°C

Adapter Temperature

225 - 270

°C

Die Temperature

225 - 270

°C

Calibrator Temperature

60 - 80

°C