Parameter
Value
Unit
性能：通用级，非溴化阻燃PC/ABS。
10
10
2016
苏州Cycoloy 非溴化阻燃PC/ABS C2950HF
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：SABIC
价格：面议
元/KG
供应地：广东省东莞市
产品型号：C2950HF
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced impact and heat properties plus improved flow for various applications.
Property
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
650
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
5
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
40
%
ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span
980
kgf/cm2
ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span
26300
kgf/cm2
ASTM D 790
Hardness, Rockwell R
121
-
ASTM D 785
IMPACT
Izod Impact, notched, 23°C
46
cm-kgf/cm
ASTM D 256
Instrumented Impact Energy @ peak, 23°C
553
cm-kgf
ASTM D 3763
THERMAL
Vicat Softening Temp, Rate B/50
112
°C
ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed
87
°C
ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed
101
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed
93
°C
ASTM D 648
CTE, -30°C to 30°C, flow
7.2E-05
1/°C
ASTM D 696
CTE, -30°C to 30°C, xflow
7.2E-05
1/°C
ASTM D 696
Thermal Conductivity
0.2
W/m-°C
ASTM C 177
Relative Temp Index, Elec
85
°C
UL 746B
Relative Temp Index, Mech w/impact
85
°C
UL 746B
Relative Temp Index, Mech w/o impact
85
°C
UL 746B
PHYSICAL
Specific Gravity
1.18
-
ASTM D 792
Water Absorption, 24 hours
0.1
%
ASTM D 570
Water Absorption, equilibrium, 23C
0.4
%
ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Melt Flow Rate, 260°C/2.16 kgf
22
g/10 min
ASTM D 1238
ELECTRICAL
Volume Resistivity
1.6E+17
Ohm-cm
ASTM D 257
Surface Resistivity
>1.E+16
Ohm
ASTM D 257
Dielectric Strength, in oil, 3.2 mm
24.3
kV/mm
ASTM D 149
Relative Permittivity, 50/60 Hz
2.8
-
ASTM D 150
Relative Permittivity, 1 MHz
2.7
-
ASTM D 150
Dissipation Factor, 50/60 Hz
0.0052
-
ASTM D 150
Dissipation Factor, 1 MHz
0.0071
-
ASTM D 150
Arc Resistance, Tungsten {PLC}
6
PLC Code
ASTM D 495
Hot Wire Ignition {PLC)
2
PLC Code
UL 746A
High Voltage Arc Track Rate {PLC}
3
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
0
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
2
PLC Code
UL 746A
FLAME CHARACTERISTICS
UL Recognized, 94V-2 Flame Class Rating (3)
0.76
mm
UL 94
UL Recognized, 94V-0 Flame Class Rating (3)
1.49
mm
UL 94
UL Recognized, 94-5VA Rating (3)
3.4
mm
UL 94
UL Recognized, 94-5VB Rating (3)
2.48
mm
UL 94
Oxygen Index (LOI)
30
%
ASTM D 2863
Source GMD, last updated:2000/01/05
Processing
Injection Molding
Drying Temperature
80 - 90
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
245 - 275
°C
Nozzle Temperature
245 - 275
°C
Front - Zone 3 Temperature
245 - 275
°C
Middle - Zone 2 Temperature
220 - 265
°C
Rear - Zone 1 Temperature
220 - 255
°C
Mold Temperature
60 - 80
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
30 - 80
%
Vent Depth
0.038 - 0.076
mm