型号：Cycoloy PC/ABS C2950
性能：通用级，非溴化阻燃PC/ABS。
CYCOLOY? Resin C2950
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 非溴化阻燃PC/ABS C2950
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：SABIC
价格：面议
元/KG
供应地：广东省东莞市
产品型号：C2950
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
Property
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
630
kgf/cm2
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
40
%
ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span
1040
kgf/cm2
ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span
27000
kgf/cm2
ASTM D 790
Hardness, Rockwell R
123
-
ASTM D 785
IMPACT
Izod Impact, notched, 23°C
54
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
16
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
622
cm-kgf
ASTM D 3763
Instrumented Impact Total Energy, -30°C
553
cm-kgf
ASTM D 3763
THERMAL
Vicat Softening Temp, Rate B/50
112
°C
ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed
90
°C
ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed
104
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed
95
°C
ASTM D 648
CTE, -30°C to 30°C, flow
7.2E-05
1/°C
ASTM D 696
CTE, -30°C to 30°C, xflow
7.2E-05
1/°C
ASTM D 696
Thermal Conductivity
0.2
W/m-°C
ASTM C 177
Relative Temp Index, Elec
85
°C
UL 746B
Relative Temp Index, Mech w/impact
85
°C
UL 746B
Relative Temp Index, Mech w/o impact
85
°C
UL 746B
PHYSICAL
Specific Gravity
1.18
-
ASTM D 792
Specific Gravity, color
1.22
-
ASTM D 792
Water Absorption, 24 hours
0.1
%
ASTM D 570
Water Absorption, equilibrium, 23C
0.4
%
ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Melt Flow Rate, 260°C/2.16 kgf
10
g/10 min
ASTM D 1238
ELECTRICAL
Volume Resistivity
1.E+17
Ohm-cm
ASTM D 257
Surface Resistivity
>1.E+16
Ohm
ASTM D 257
Dielectric Strength, in oil, 3.2 mm
19.4
kV/mm
ASTM D 149
Relative Permittivity, 50/60 Hz
3
-
ASTM D 150
Relative Permittivity, 100 Hz
3
-
ASTM D 150
Dissipation Factor, 50/60 Hz
0.005
-
ASTM D 150
Dissipation Factor, 100 Hz
0.0049
-
ASTM D 150
Arc Resistance, Tungsten {PLC}
6
PLC Code
ASTM D 495
Hot Wire Ignition {PLC)
1
PLC Code
UL 746A
High Voltage Arc Track Rate {PLC}
2
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
0
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
1
PLC Code
UL 746A
FLAME CHARACTERISTICS
UL Recognized, 94V-0 Flame Class Rating (3)
1.49
mm
UL 94
UL Recognized, 94-5VB Rating (3)
2.48
mm
UL 94
Oxygen Index (LOI)
32
%
ASTM D 2863
Source GMD, last updated:2000/01/05
Processing
Injection Molding
Drying Temperature
80 - 90
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
245 - 275
°C
Nozzle Temperature
245 - 275
°C
Front - Zone 3 Temperature
245 - 275
°C
Middle - Zone 2 Temperature
220 - 275
°C
Rear - Zone 1 Temperature
220 - 255
°C
Mold Temperature
60 - 80
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
30 - 80
%
Vent Depth
0.038 - 0.076
mm