型号：Cycoloy PC/ABS C2805
性能：阻燃级，非溴化阻燃Cycoloy PC/ABS。耐磨，阻燃化合物。
CYCOLOY? Resin C2805
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 非溴化阻燃PC/ABS C2805
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：Cycoloy
价格：面议
元/KG
供应地：广东省东莞市
产品型号：C2805
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
LNP* Lubricomp* Cycoloy* C2805 compound is a PTFE reinforced PC+ABS, wear resistant, flame retardant compound for moving components in business equipment. Medium heat performance
Property
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
630
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
520
kgf/cm2
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
110
%
ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span
970
kgf/cm2
ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span
27700
kgf/cm2
ASTM D 790
K-factor xE-10, PV=2000 psi-fpm vs Steel
430
-
SABIC Method
Coefficient of Friction on steel, Static
0.16
-
ASTM D 1894
Coefficient of Friction on steel,Kinetic
0.21
-
ASTM D 1894
IMPACT
Izod Impact, notched, 23°C
13
cm-kgf/cm
ASTM D 256
THERMAL
HDT, 1.82 MPa, 6.4 mm, unannealed
82
°C
ASTM D 648
Relative Temp Index, Elec
60
°C
UL 746B
Relative Temp Index, Mech w/impact
60
°C
UL 746B
Relative Temp Index, Mech w/o impact
60
°C
UL 746B
PHYSICAL
Specific Gravity
1.22
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.4 - 0.5
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.3 - 0.5
%
SABIC Method
ELECTRICAL
Hot Wire Ignition {PLC)
3
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
0
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
1
PLC Code
UL 746A
FLAME CHARACTERISTICS
UL Recognized, 94V-0 Flame Class Rating (3)
1.5
mm
UL 94
UL Recognized, 94-5VB Rating (3)
2.49
mm
UL 94
Source GMD, last updated:2011/09/19
Processing
Injection Molding
Drying Temperature
75 - 80
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
230 - 275
°C
Nozzle Temperature
230 - 275
°C
Front - Zone 3 Temperature
225 - 275
°C
Middle - Zone 2 Temperature
215 - 260
°C
Rear - Zone 1 Temperature
210 - 255
°C
Mold Temperature
50 - 70
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
30 - 80
%
Vent Depth
0.038 - 0.076
mm