型号：Cycoloy PC/ABS C1200HF
性能：通用级，Cycoloy PC/ABS，优秀的高耐热性，低温延性。
CYCOLOY? Resin C1200HF
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 低温延性PC/ABS C1200HF
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：Cycoloy
价格：面议
元/KG
供应地：广东省东莞市
产品型号：C1200HF
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility. For automotive, appliance and electrical components.
Property
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
580
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
5
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
150
%
ASTM D 638
Tensile Modulus, 50 mm/min
23200
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
890
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
23900
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
55
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
4.8
%
ISO 527
Tensile Strain, break, 50 mm/min
114
%
ISO 527
Tensile Modulus, 1 mm/min
2360
MPa
ISO 527
Flexural Stress
86
MPa
ISO 178
Flexural Modulus
2250
MPa
ISO 178
IMPACT
Izod Impact, notched, 23°C
59
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
49
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
553
cm-kgf
ASTM D 3763
Instrumented Impact Total Energy, -30°C
553
cm-kgf
ASTM D 3763
Izod Impact, notched, 23°C, 80*10*4mm, Cut
49
kJ/m2
ISO 180/1A
Izod Impact, notched, -30°C, 80*10*4mm, Cut
34
kJ/m2
ISO 180/1A
THERMAL
HDT, 0.45 MPa, 3.2 mm, unannealed
129
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
112
°C
ASTM D 648
CTE, -40°C to 40°C, flow
7.2E-05
1/°C
ASTM E 831
Vicat Softening Temp, Rate B/50
130
°C
ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
130
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
110
°C
ISO 75/Af
Relative Temp Index, Elec
105
°C
UL 746B
Relative Temp Index, Mech w/impact
80
°C
UL 746B
Relative Temp Index, Mech w/o impact
105
°C
UL 746B
PHYSICAL
Specific Gravity
1.15
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.5 - 0.7
%
SABIC Method
Melt Flow Rate, 260°C/5.0 kgf
19
g/10 min
ASTM D 1238
Melt Volume Rate, MVR at 265°C/5.0 kg
24
cm3/10 min
ISO 1133
ELECTRICAL
Hot Wire Ignition {PLC)
3
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
1
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
2
PLC Code
UL 746A
FLAME CHARACTERISTICS
UL Recognized, 94HB Flame Class Rating (3)
1.19
mm
UL 94
Source GMD, last updated:2013/03/15
Processing
Injection Molding
Drying Temperature
100 - 110
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
275 - 300
°C
Nozzle Temperature
275 - 300
°C
Front - Zone 3 Temperature
260 - 300
°C
Middle - Zone 2 Temperature
255 - 295
°C
Rear - Zone 1 Temperature
250 - 290
°C
Hopper Temperature
60 - 80
°C
Mold Temperature
60 - 90
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
30 - 80
%
Vent Depth
0.038 - 0.076
mm