品牌：Cycoloy

价格：面议元/KG

供应地：广东省东莞市

产品型号：C1200

型号：Cycoloy PC/ABS C1200

性能：通用级，Cycoloy PC/ABS，优秀的高抗热性，低温延性

CYCOLOY? Resin C1200

| British

| Metric

| PDF

Americas: COMMERCIAL

PC+ABS, excellent impact/high heat resistance. Low temperature ductility. For automotive, appliance and electrical components.

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	610	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	150	%	ASTM D 638
Tensile Modulus, 50 mm/min	23200	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	890	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	23900	kgf/cm2	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	65	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	54	cm-kgf/cm	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	622	cm-kgf	ASTM D 3763
Instrumented Impact Energy @ peak, -30	622	cm-kgf	ASTM D 3763
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	129	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	112	°C	ASTM D 648
CTE, -40°C to 40°C, flow	7.2E-05	1/°C	ASTM E 831
Vicat Softening Temp, Rate B/50	130	°C	ISO 306
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.15	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)	0.5 - 0.7	%	SABIC Method
Melt Flow Rate, 260°C/5.0 kgf	11.4	g/10 min	ASTM D 1238
ELECTRICAL	Value	Unit	Standard
Hot Wire Ignition {PLC)	3	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	1	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	2	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	1.19	mm	UL 94

Source GMD, last updated:2000/01/05