型号：Cycoloy PC/ABS MC1300
性能：电镀级，Cycoloy PC/ABS，汽车，专为电镀应用。
CYCOLOY? Resin MC1300
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 电镀应用PC/ABS MC1300 电镀级
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：SABIC
价格：面议
元/KG
供应地：广东省东莞市
产品型号：MC1300
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
Cycoloy MC1300 resin is an injection moldable PC/ABS blend with excellent flow and impact performance. It is designed for plating applications mostly used in the automotive industry.
Property
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
510
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
440
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
8.6
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
150
%
ASTM D 638
Tensile Modulus, 50 mm/min
21700
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
730
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
21000
kgf/cm2
ASTM D 790
IMPACT
Izod Impact, notched, 23°C
54
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
43
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
414
cm-kgf
ASTM D 3763
Instrumented Impact Total Energy, -30°C
345
cm-kgf
ASTM D 3763
THERMAL
Vicat Softening Temp, Rate B/50
111
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
115
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
98
°C
ASTM D 648
CTE, -40°C to 40°C, flow
7.2E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
9.E-05
1/°C
ASTM E 831
Thermal Conductivity
0.2
W/m-°C
ASTM C 177
PHYSICAL
Specific Gravity
1.1
-
ASTM D 792
Water Absorption, 24 hours
0.1
%
ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5)
0.5 - 0.8
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.5 - 0.7
%
SABIC Method
Melt Flow Rate, 260°C/5.0 kgf
14
g/10 min
ASTM D 1238
Source GMD, last updated:1998/10/05
Processing
Injection Molding
Drying Temperature
100 - 105
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
260 - 290
°C
Nozzle Temperature
260 - 290
°C
Front - Zone 3 Temperature
255 - 290
°C
Middle - Zone 2 Temperature
255 - 290
°C
Rear - Zone 1 Temperature
250 - 280
°C
Mold Temperature
75 - 100
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
30 - 80
%
Vent Depth
0.038 - 0.076
mm