CYCOLOY? Resin CY6310

Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or large size applications including business equipment, enclosures, among others.

Tensile Stress, yld, Type I, 50 mm/min

640

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

500

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

4.2

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

>50

%

ASTM D 638

Tensile Modulus, 5 mm/min

27500

kgf/cm2

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

1020

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

27500

kgf/cm2

ASTM D 790

Tensile Stress, yield, 50 mm/min

63

MPa

ISO 527

Tensile Stress, break, 50 mm/min

51

MPa

ISO 527

Tensile Strain, yield, 50 mm/min

4.4

%

ISO 527

Tensile Strain, break, 50 mm/min

>50

%

ISO 527

Tensile Modulus, 1 mm/min

2700

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

91

MPa

ISO 178

Flexural Modulus, 2 mm/min

2650

MPa

ISO 178

Izod Impact, notched, 23°C

61

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

11

cm-kgf/cm

ASTM D 256

Multiaxial Impact

1070

cm-kgf

ISO 6603

Instrumented Impact Total Energy, 23°C

662

cm-kgf

ASTM D 3763

Izod Impact, unnotched 80*10*3 +23°C

NB

kJ/m2

ISO 180/1U

Izod Impact, notched 80*10*3 +23°C

50

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*3 -30°C

13

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm

55

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm

14

kJ/m2

ISO 179/1eA

Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm

NB

kJ/m2

ISO 179/1eU

Vicat Softening Temp, Rate B/50

109

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed

100

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

88

°C

ASTM D 648

CTE, -40°C to 40°C, flow

6.8E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

7.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, flow

6.8E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

7.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 75°C +/- 2°C

Pass

-

IEC 60695-10-2

Ball Pressure Test, approximate maximum

95

°C

IEC 60695-10-2

Vicat Softening Temp, Rate B/50

109

°C

ISO 306

Vicat Softening Temp, Rate B/120

111

°C

ISO 306

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

90

°C

ISO 75/Af

Relative Temp Index, Elec

85

°C

UL 746B

Relative Temp Index, Mech w/impact

85

°C

UL 746B

Relative Temp Index, Mech w/o impact

85

°C

UL 746B

Specific Gravity

1.16

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.4 - 0.6

%

SABIC Method

Melt Flow Rate, 250°C/2.16 kgf

16

g/10 min

ASTM D 1238

Melt Flow Rate, 260°C/2.16 kgf

20

g/10 min

ASTM D 1238

Density

1.16

g/cm3

ISO 1183

Water Absorption, (23°C/sat)

0.6

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.2

%

ISO 62

Melt Volume Rate, MVR at 260°C/2.16 kg

19

cm3/10 min

ISO 1133

Hot Wire Ignition {PLC)

3

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC}

0

PLC Code

UL 746A

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity, ROA

>1.E+15

Ohm

IEC 60093

Comparative Tracking Index

575

V

IEC 60112

UL Compliant, 94V-2 Flame Class Rating (3)(4)

0.75

mm

UL 94 by SABIC-IP

UL Compliant, 94V-0 Flame Class Rating (3)(4)

1.5

mm

UL 94 by SABIC-IP

UL Compliant, 94-5VA Rating (3)(4)

2.9

mm

UL 94 by SABIC-IP

UL Compliant, 94-5VB Rating (3)(4)

2.3

mm

UL 94 by SABIC-IP

UL Recognized, 94V-2 Flame Class Rating (3)

0.75

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating (3)

1.5

mm

UL 94

UL Recognized, 94-5VA Rating (3)

2.9

mm

UL 94

UL Recognized, 94-5VB Rating (3)

2.3

mm

UL 94

Glow Wire Flammability Index 960°C, passes at

3

mm

IEC 60695-2-12

Oxygen Index (LOI)

30

%

ISO 4589

Source GMD, last updated:2007/08/16

Drying Temperature

90 - 100

°C

Drying Time

2 - 4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250 - 280

°C

Nozzle Temperature

230 - 270

°C

Front - Zone 3 Temperature

240 - 280

°C

Middle - Zone 2 Temperature

230 - 270

°C

Rear - Zone 1 Temperature

210 - 240

°C

Hopper Temperature

60 - 80

°C

Mold Temperature

60 - 90

°C