型号：Cycoloy PC/ABS CX7240U
性能：注塑级，注射可塑造的PC/ABS混合，紫外线稳定。
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 紫外线稳定PC/ABS CX7240U
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：沙伯基础
价格：面议
元/KG
供应地：广东省东莞市
产品型号：CX7240U
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
660
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
590
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
4.1
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
100
%
ASTM D 638
Tensile Modulus, 50 mm/min
30000
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
1060
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
28000
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
65
MPa
ISO 527
Tensile Stress, break, 50 mm/min
50
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
4
%
ISO 527
Tensile Strain, break, 50 mm/min
90
%
ISO 527
Tensile Modulus, 1 mm/min
2530
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
96
MPa
ISO 178
Flexural Modulus, 2 mm/min
2500
MPa
ISO 178
IMPACT
Izod Impact, notched, 23°C
50
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
10
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
662
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*3 +23°C
20
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*3 -30°C
10
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
20
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
10
kJ/m2
ISO 179/1eA
THERMAL
Vicat Softening Temp, Rate B/50
106
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
100
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
89
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed
99
°C
ASTM D 648
CTE, -40°C to 40°C, flow
6.25E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
5.35E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow
6.2E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
5.4E-05
1/°C
ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C
PASS
-
IEC 60695-10-2
Vicat Softening Temp, Rate B/50
110
°C
ISO 306
Vicat Softening Temp, Rate B/120
113
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
93
°C
ISO 75/Af
Relative Temp Index, Elec
90
°C
UL 746B
Relative Temp Index, Mech w/impact
90
°C
UL 746B
Relative Temp Index, Mech w/o impact
90
°C
UL 746B
PHYSICAL
Specific Gravity
1.19
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Melt Flow Rate, 260°C/2.16 kgf
16
g/10 min
ASTM D 1238
Density
1.2
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.2
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.1
%
ISO 62
Melt Volume Rate, MVR at 260°C/2.16 kg
15
cm3/10 min
ISO 1133
ELECTRICAL
Hot Wire Ignition {PLC)
3
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
0
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
3
PLC Code
UL 746A
FLAME CHARACTERISTICS
UL Recognized, 94V-2 Flame Class Rating (3)
0.4
mm
UL 94
UL Recognized, 94V-1 Flame Class Rating (3)
0.6
mm
UL 94
UL Recognized, 94V-0 Flame Class Rating (3)
0.75
mm
UL 94
UL Recognized, 94-5VA Rating (3)
3
mm
UL 94
UL Recognized, 94-5VB Rating (3)
1.5
mm
UL 94
Glow Wire Flammability Index 960°C, passes at
0.75
mm
IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm
825
°C
IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm
800
°C
IEC 60695-2-13
Source GMD, last updated:2007/05/30
Processing
Injection Molding
Drying Temperature
90
°C
Drying Time
4
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
270 - 300
°C
Nozzle Temperature
265 - 300
°C
Front - Zone 3 Temperature
265 - 300
°C
Middle - Zone 2 Temperature
260 - 300
°C
Rear - Zone 1 Temperature
260 - 300
°C
Hopper Temperature
60 - 80
°C
Mold Temperature
60 - 90
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
40 - 80
%
Vent Depth
0.038 - 0.076
mm