型号：Cycoloy PC/ABS CP8930
性能：电镀级，可电镀Cycoloy PC/ABS。
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 可电镀PC/ABS CP8930
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：沙伯基础
价格：面议
元/KG
供应地：广东省东莞市
产品型号：CP8930
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
530
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
470
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
4.2
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
110
%
ASTM D 638
Tensile Modulus, 5 mm/min
24100
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
830
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
24100
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
51
MPa
ISO 527
Tensile Stress, break, 50 mm/min
47
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
4
%
ISO 527
Tensile Strain, break, 50 mm/min
100
%
ISO 527
Tensile Modulus, 1 mm/min
2400
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
65
MPa
ISO 178
Flexural Modulus, 2 mm/min
2200
MPa
ISO 178
IMPACT
Izod Impact, notched, 23°C
57
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
38
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
560
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*3 +23°C
50
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*3 -30°C
35
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
50
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
35
kJ/m2
ISO 179/1eA
THERMAL
Vicat Softening Temp, Rate B/50
126
°C
ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed
103
°C
ASTM D 648
CTE, -40°C to 40°C, flow
7.2E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
7.8E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow
7.2E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
7.8E-05
1/°C
ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C
PASSES
-
IEC 60695-10-2
Vicat Softening Temp, Rate B/50
126
°C
ISO 306
Vicat Softening Temp, Rate B/120
129
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
103
°C
ISO 75/Af
PHYSICAL
Specific Gravity
1.13
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.5 - 0.8
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.5 - 0.7
%
SABIC Method
Melt Flow Rate, 260°C/5.0 kgf
16
g/10 min
ASTM D 1238
Density
1.1
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.4
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.2
%
ISO 62
Melt Volume Rate, MVR at 265°C/5.0 kg
20
cm3/10 min
ISO 1133
Source GMD, last updated:2004/12/21
Processing
Injection Molding
Drying Temperature
100 - 105
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
260 - 290
°C
Nozzle Temperature
260 - 290
°C
Front - Zone 3 Temperature
255 - 290
°C
Middle - Zone 2 Temperature
255 - 290
°C
Rear - Zone 1 Temperature
250 - 280
°C
Mold Temperature
75 - 100
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
30 - 80
%
Vent Depth
0.038 - 0.076
mm