型号：Cycoloy PC/ABS CP8320
性能：电镀级，电镀级Cycoloy PC/ABS。
CYCOLOY? Resin CP8320
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 电镀级PC/ABS CP8320
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：SABIC
价格：面议
元/KG
供应地：广东省东莞市
产品型号：CP8320
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
Cycoloy Medium Heat Plating Grade for Automotive
Property
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
450
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
400
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
4
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
100
%
ASTM D 638
Tensile Modulus, 5 mm/min
21400
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
710
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
20300
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
45
MPa
ISO 527
Tensile Stress, break, 50 mm/min
40
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
4
%
ISO 527
Tensile Strain, break, 50 mm/min
100
%
ISO 527
Tensile Modulus, 1 mm/min
2100
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
65
MPa
ISO 178
Flexural Modulus, 2 mm/min
2000
MPa
ISO 178
IMPACT
Izod Impact, notched, 23°C
61
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
40
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
560
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*3 +23°C
60
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*3 -30°C
30
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
60
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
30
kJ/m2
ISO 179/1eA
THERMAL
Vicat Softening Temp, Rate B/50
106
°C
ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed
90
°C
ASTM D 648
CTE, -40°C to 40°C, flow
9.E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
9.E-05
1/°C
ASTM E 831
Thermal Conductivity
0.2
W/m-°C
ISO 8302
CTE, -40°C to 40°C, flow
9.E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
9.E-05
1/°C
ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C
Pass
-
IEC 60695-10-2
Vicat Softening Temp, Rate B/50
106
°C
ISO 306
Vicat Softening Temp, Rate B/120
107
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
92
°C
ISO 75/Af
PHYSICAL
Specific Gravity
1.1
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.5 - 0.7
%
SABIC Method
Melt Flow Rate, 260°C/5.0 kgf
14
g/10 min
ASTM D 1238
Density
1.1
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.3
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.1
%
ISO 62
Melt Volume Rate, MVR at 260°C/5.0 kg
13
cm3/10 min
ISO 1133
ELECTRICAL
Volume Resistivity
>1.E+15
Ohm-cm
IEC 60093
Surface Resistivity, ROA
>1.E+15
Ohm
IEC 60093
Dielectric Strength, in oil, 0.8 mm
35
kV/mm
IEC 60243-1
Dielectric Strength, in oil, 1.6 mm
25
kV/mm
IEC 60243-1
Dielectric Strength, in oil, 3.2 mm
17
kV/mm
IEC 60243-1
Source GMD, last updated:2006/06/14
Processing
Injection Molding
Drying Temperature
95 - 105
°C
Drying Time
2 - 4
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
250 - 280
°C
Nozzle Temperature
230 - 270
°C
Front - Zone 3 Temperature
240 - 280
°C
Middle - Zone 2 Temperature
240 - 280
°C
Rear - Zone 1 Temperature
220 - 250
°C
Hopper Temperature
60 - 80
°C
Mold Temperature
60 - 90
°C