型号：Cycoloy PC/ABS CM6210
性能：通用级，PC/ABS，高模量。
CYCOLOY? Resin CM6210
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 高模量PC/ABS CM6210
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：SABIC
价格：面议
元/KG
供应地：广东省东莞市
产品型号：CM6210
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection molding applications where higher stiffness is needed.
Property
MECHANICAL
Tensile Stress, yld, Type I, 5 mm/min
650
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min
500
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min
4.9
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
80
%
ASTM D 638
Tensile Modulus, 5 mm/min
36400
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
1120
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
35600
kgf/cm2
ASTM D 790
Tensile Stress, yield, 5 mm/min
59
MPa
ISO 527
Tensile Stress, break, 5 mm/min
65
MPa
ISO 527
Tensile Stress, yield, 50 mm/min
63
MPa
ISO 527
Tensile Stress, break, 50 mm/min
50
MPa
ISO 527
Tensile Strain, yield, 5 mm/min
3.6
%
ISO 527
Tensile Strain, break, 5 mm/min
101
%
ISO 527
Tensile Strain, yield, 50 mm/min
3.5
%
ISO 527
Tensile Strain, break, 50 mm/min
97
%
ISO 527
Tensile Modulus, 1 mm/min
3660
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
106
MPa
ISO 178
Flexural Modulus, 2 mm/min
3560
MPa
ISO 178
Hardness, Rockwell R
98
-
ISO 2039-2
IMPACT
Izod Impact, notched, 23°C
50
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
9
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
458
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*3 +23°C
45
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*3 -30°C
10
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
45
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
10
kJ/m2
ISO 179/1eA
THERMAL
Vicat Softening Temp, Rate B/50
106
°C
ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed
90
°C
ASTM D 648
CTE, -40°C to 40°C, flow
5.7E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
7.E-05
1/°C
ASTM E 831
Thermal Conductivity
0.3
W/m-°C
ISO 8302
CTE, -40°C to 40°C, flow
5.2E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
6.E-05
1/°C
ISO 11359-2
CTE, 23°C to 60°C, flow
5.2E-05
1/°C
ISO 11359-2
CTE, 23°C to 60°C, xflow
6.E-05
1/°C
ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C
pass
-
IEC 60695-10-2
Ball Pressure Test, approximate maximum
95
°C
IEC 60695-10-2
Vicat Softening Temp, Rate B/50
112
°C
ISO 306
Vicat Softening Temp, Rate B/120
114
°C
ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
99
°C
ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
89
°C
ISO 75/Ae
Relative Temp Index, Elec
60
°C
UL 746B
Relative Temp Index, Mech w/impact
60
°C
UL 746B
Relative Temp Index, Mech w/o impact
60
°C
UL 746B
PHYSICAL
Specific Gravity
1.28
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.4 - 0.6
%
SABIC Method
Melt Flow Rate, 260°C/5.0 kgf
11.5
g/10 min
ASTM D 1238
Density
1.27
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.3
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.1
%
ISO 62
Melt Volume Rate, MVR at 260°C/5.0 kg
9
cm3/10 min
ISO 1133
ELECTRICAL
Dielectric Strength, in oil, 0.8 mm
38
kV/mm
IEC 60243-1
Dielectric Strength, in oil, 1.6 mm
26
kV/mm
IEC 60243-1
Dielectric Strength, in oil, 3.2 mm
17
kV/mm
IEC 60243-1
Relative Permittivity, 1 MHz
2.8
-
IEC 60250
Dissipation Factor, 50/60 Hz
0.003
-
IEC 60250
Dissipation Factor, 1 MHz
0.004
-
IEC 60250
Comparative Tracking Index
250
V
IEC 60112
Relative Permittivity, 50/60 Hz
2.9
-
IEC 60250
FLAME CHARACTERISTICS
UL Recognized, 94V-0 Flame Class Rating (3)
1.5
mm
UL 94
Source GMD, last updated:2005/02/08
Processing
? Barrel temperatures should be banked TO 150°C (300°F)
Sheet Extrusion
Drying Temperature
80 - 90
°C
Drying Time
3 - 4
hrs
Drying Time (Cumulative)
12
hrs
Minimum Moisture Content
0.04
%
Melt Temperature
220 - 245
°C
Barrel - Zone 1 Temperature
180 - 225
°C
Barrel - Zone 2 Temperature
190 - 230
°C
Barrel - Zone 3 Temperature
205 - 240
°C
Barrel - Zone 4 Temperature
210 - 245
°C
Adapter Temperature
210 - 245
°C
Die Temperature
210 - 245
°C
Roll Stack Temp - Top
70 - 100
°C
Roll Stack Temp - Middle
70 - 95
°C
Roll Stack Temp - Bottom
65 - 90
°C