型号：Cycoloy PC/ABS CH6410
性能：通用级，耐高温，冲击改性树脂，阻燃。
CYCOLOY? Resin CH6410
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 耐高温PC/ABS CH6410
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：SABIC
价格：面议
元/KG
供应地：广东省东莞市
产品型号：CH6410
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
CH6410 is a high heat, impact modified PC resin, with nonbrominated, nonchlorinated flame retardant system. Limited colors only.
Property
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min
640
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
550
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
5.5
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
88
%
ASTM D 638
Tensile Modulus, 50 mm/min
25900
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
970
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
26500
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
63
MPa
ISO 527
Tensile Stress, break, 50 mm/min
55
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
5
%
ISO 527
Tensile Strain, break, 50 mm/min
95
%
ISO 527
Tensile Modulus, 1 mm/min
2300
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
90
MPa
ISO 178
Flexural Modulus, 2 mm/min
2400
MPa
ISO 178
Hardness, H358/30
100
MPa
ISO 2039-1
IMPACT
Izod Impact, notched, 23°C
92
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
740
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*4 +23°C
50
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*4 0°C
19
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*4 -30°C
15
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
55
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
15
kJ/m2
ISO 179/1eA
THERMAL
HDT, 0.45 MPa, 3.2 mm, unannealed
127
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
118
°C
ASTM D 648
CTE, -40°C to 40°C, flow
7.74E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
5.94E-05
1/°C
ASTM E 831
CTE, 23°C to 60°C, flow
7.E-05
1/°C
ISO 11359-2
CTE, 23°C to 60°C, xflow
7.E-05
1/°C
ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES
-
IEC 60695-10-2
Vicat Softening Temp, Rate B/50
134
°C
ISO 306
Vicat Softening Temp, Rate B/120
135
°C
ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
126
°C
ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
113
°C
ISO 75/Ae
PHYSICAL
Specific Gravity
1.19
-
ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) (5)
0.05 - 0.07
%
SABIC Method
Mold Shrinkage, flow, 3.2 mm (5)
0.4 - 0.5
%
SABIC Method
Melt Flow Rate, 260°C/2.16 kgf
6.3
g/10 min
ASTM D 1238
Density
1.2
g/cm3
ISO 1183
Melt Volume Rate, MVR at 260°C/5.0 kg
16
cm3/10 min
ISO 1133
ELECTRICAL
Volume Resistivity
>1.E+15
Ohm-cm
IEC 60093
Surface Resistivity, ROA
>1.E+15
Ohm
IEC 60093
Dielectric Strength, in oil, 3.2 mm
18
kV/mm
IEC 60243-1
Relative Permittivity, 1 MHz
2.7
-
IEC 60250
Dissipation Factor, 50/60 Hz
0.001
-
IEC 60250
Dissipation Factor, 1 MHz
0.01
-
IEC 60250
Comparative Tracking Index
225
V
IEC 60112
Relative Permittivity, 50/60 Hz
2.7
-
IEC 60250
FLAME CHARACTERISTICS
UL Recognized, 94V-1 Flame Class Rating (3)
0.99
mm
UL 94
UL Recognized, 94V-0 Flame Class Rating (3)
1.49
mm
UL 94
Source GMD, last updated:2002/10/29
Processing
Injection Molding
Drying Temperature
90 - 100
°C
Drying Time
2 - 4
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.04
%
Melt Temperature
270 - 300
°C
Nozzle Temperature
265 - 300
°C
Front - Zone 3 Temperature
265 - 300
°C
Middle - Zone 2 Temperature
260 - 300
°C
Rear - Zone 1 Temperature
260 - 300
°C
Mold Temperature
60 - 90
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
40 - 80
%
Vent Depth
0.038 - 0.076
mm