型号：Cycoloy PC/ABS CE1821
性能：挤出级，高刚度PC/ABS混合，耐高温，低CTE，挤压和热成型特点。
CYCOLOY? Resin CE1821
TYPICAL PROPERTIES (1)
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Value
Unit
Standard
Parameter
Value
Unit
Parameter
Value
Unit
10
10
2016
苏州Cycoloy 耐高温PC/ABS CE1821
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：SABIC
价格：面议
元/KG
供应地：广东省东莞市
产品型号：CE1821
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
High stiffness PC/ABS blend offering high impact, high heat, low CTE, good surface quality and excellent extrusion and thermoforming characteristics.
Property
MECHANICAL
Tensile Stress, yld, Type I, 5 mm/min
610
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min
560
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min
5
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
110
%
ASTM D 638
Tensile Modulus, 5 mm/min
31600
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
960
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
30500
kgf/cm2
ASTM D 790
Tensile Stress, yield, 5 mm/min
60
MPa
ISO 527
Tensile Stress, break, 5 mm/min
55
MPa
ISO 527
Tensile Strain, yield, 5 mm/min
5
%
ISO 527
Tensile Strain, break, 5 mm/min
110
%
ISO 527
Tensile Modulus, 1 mm/min
3100
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
95
MPa
ISO 178
Flexural Modulus, 2 mm/min
3000
MPa
ISO 178
IMPACT
Izod Impact, notched, 23°C
50
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
12
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
662
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*3 +23°C
45
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*3 -30°C
10
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
45
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
10
kJ/m2
ISO 179/1eA
THERMAL
Vicat Softening Temp, Rate B/50
138
°C
ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed
120
°C
ASTM D 648
CTE, -40°C to 40°C, flow
6.E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
7.E-05
1/°C
ASTM E 831
Thermal Conductivity
0.2
W/m-°C
ISO 8302
CTE, -40°C to 40°C, flow
6.E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
7.E-05
1/°C
ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES
-
IEC 60695-10-2
Vicat Softening Temp, Rate B/50
138
°C
ISO 306
Vicat Softening Temp, Rate B/120
140
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
120
°C
ISO 75/Af
PHYSICAL
Specific Gravity
1.22
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.5 - 0.7
%
SABIC Method
Melt Flow Rate, 260°C/5.0 kgf
12
g/10 min
ASTM D 1238
Density
1.22
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.4
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.1
%
ISO 62
Melt Volume Rate, MVR at 260°C/5.0 kg
10
cm3/10 min
ISO 1133
Source GMD, last updated:2005/11/29
Processing
Injection Molding
Drying Temperature
120 - 110
°C
Drying Time
2 - 6
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
270 - 300
°C
Nozzle Temperature
260 - 290
°C
Front - Zone 3 Temperature
270 - 300
°C
Middle - Zone 2 Temperature
265 - 290
°C
Rear - Zone 1 Temperature
260 - 270
°C
Mold Temperature
60 - 100
°C
Back Pressure
0.3 - 0.7
MPa
Screw Speed
40 - 70
rpm
Shot to Cylinder Size
30 - 80
%
Vent Depth
0.038 - 0.076
mm
Sheet Extrusion
Drying Temperature
120 - 120
°C
Drying Time
2 - 6
hrs
Drying Time (Cumulative)
8
hrs
Maximum Moisture Content
0.02
%
Melt Temperature
250 - 270
°C
Barrel - Zone 1 Temperature
195 - 205
°C
Barrel - Zone 2 Temperature
200 - 220
°C
Barrel - Zone 3 Temperature
220 - 240
°C
Barrel - Zone 4 Temperature
230 - 260
°C
Adapter Temperature
230 - 260
°C
Die Temperature
230 - 245
°C
Roll Stack Temp - Top
100 - 110
°C
Roll Stack Temp - Middle
110 - 120
°C
Roll Stack Temp - Bottom
145 - 155
°C