Bayblend W85XF
未增强注塑级，耐候性改良，优化的热老化稳定，易流动，高耐热性，维卡/乙120 = 132℃
[Datasheet Bayblend W85 XF]
Disclaimer
PC/ABS
良好的流动性良好的耐热老化性;好Weathe ...
Property
Test Condition
Unit
Standard
typical Value
Rheological properties
Melt volume-flow rate
260 °C; 5 kg
cm3/10 min
ISO 1133
27
Molding shrinkage, parallel
150x105x3 mm; 260 °C / MT 80 °C
%
b.o. ISO 2577
0.55 - 0.75
Molding shrinkage, normal
150x105x3 mm; 260 °C / MT 80 °C
%
b.o. ISO 2577
0.55 - 0.75
Melt viscosity
1000 s-1; 260 °C
Pa·s
b.o. ISO 11443-A
225
Mechanical properties (23 °C/50 % r. h.)
Tensile modulus
1 mm/min
MPa
ISO 527-1,-2
2450
Yield stress
50 mm/min
MPa
ISO 527-1,-2
63
Yield strain
50 mm/min
%
ISO 527-1,-2
5.0
Stress at break
50 mm/min
MPa
ISO 527-1,-2
62
Strain at break
50 mm/min
%
b.o. ISO 527-1,-2
> 50
Izod impact strength
23 °C
kJ/m2
ISO 180-U
N
Izod impact strength
-30 °C
kJ/m2
ISO 180-U
N
Izod notched impact strength
23 °C
kJ/m2
ISO 180-A
45
Izod notched impact strength
-20 °C
kJ/m2
ISO 180-A
15
Thermal properties
Temperature of deflection under load
1.80 MPa
°C
ISO 75-1,-2
109
Temperature of deflection under load
0.45 MPa
°C
ISO 75-1,-2
127
Vicat softening temperature
50 N; 50 °C/h
°C
ISO 306
130
Vicat softening temperature
50 N; 120 °C/h
°C
ISO 306
132
Coefficient of linear thermal expansion, parallel
23 to 55 °C
10-4/K
ISO 11359-1,-2
0.7
Coefficient of linear thermal expansion, transverse
23 to 55 °C
10-4/K
ISO 11359-1,-2
0.7
Burning behavior UL 94 [UL recognition]
0.85 mm
Class
UL 94
HB
Electrical properties (23 °C/50 % r. h.)
Relative permittivity
100 Hz
-
IEC 60250
3.1
Relative permittivity
1 MHz
-
IEC 60250
2.8
Dissipation factor
100 Hz
10-4
IEC 60250
25
Dissipation factor
1 MHz
10-4
IEC 60250
105
Volume resistivity
Ohm·m
IEC 60093
1E14
Surface resistivity
Ohm
IEC 60093
1E16
Electrical strength
1 mm
kV/mm
IEC 60243-1
35
Comparative tracking index CTI
Solution A
Rating
IEC 60112
225
Other properties (23 °C)
Water absorption (saturation value)
Water at 23 °C
%
ISO 62
0.5
Water absorption (equilibrium value)
23 °C; 50 % r. h.
%
ISO 62
0.2
Density
kg/m3
ISO 1183-1
1160
Processing conditions for test specimens
Injection molding-Melt temperature
°C
ISO 294
260
Injection molding-Mold temperature
°C
ISO 294
80
Injection molding-Injection velocity
mm/s
ISO 294
240
10
10
2016
苏州Bayblend 高耐热性W85XF
来源:[东莞市大田化工有限公司]
联系人：赵先生
手机：13662889445
电话：0769-84393119
传真：0769-84393119
QQ：286928167
Email：1423969852@qq.com
地址：广东省东莞市东莞市常平司马管理区洲寮新街二十三号
品牌：Bayblend
价格：面议
元/KG
供应地：广东省东莞市
产品型号：W85XF