Bayblend FR3030
PC/ABS
无卤阻燃，

挤出级，维卡/乙120温度= 115°C;良好的挤出和真空成型的行为;  UL认可94 V-0（1.5毫米），无卤素DIN VDE 0472,815（GWFI），灼热丝温度：960℃在1.0毫米。

[Datasheet Bayblend FR3030]

Property		Test Condition	Unit	Standard	typical Value
Rheological properties
	Melt volume-flow rate	260 °C; 5 kg	cm3/10 min	ISO 1133	11
	Molding shrinkage, parallel	150x105x3 mm; 260 °C / MT 80 °C	%	b.o. ISO 2577	0.5 - 0.7
	Molding shrinkage, normal	150x105x3 mm; 260 °C / MT 80 °C	%	b.o. ISO 2577	0.5 - 0.7
	Melt viscosity	1000 s-1; 260 °C	Pa·s	b.o. ISO 11443-A	410
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	2650
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	69
	Yield strain	50 mm/min	%	ISO 527-1,-2	5
	Stress at break	50 mm/min	MPa	ISO 527-1,-2	53
	Strain at break	50 mm/min	%	b.o. ISO 527-1,-2	> 50
	Izod impact strength	23 °C	kJ/m2	ISO 180-U	N
	Izod notched impact strength	23 °C	kJ/m2	ISO 180-A	40
	Izod notched impact strength	-30 °C	kJ/m2	ISO 180-A	10
Thermal properties
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	98
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	106
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	113
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	115
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.68
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.72
	Burning behavior UL 94 (1.5 mm) [UL recognition]	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V [UL recognition]	2.0 mm	Class	UL 94	5VB
	Burning behavior UL 94-5V [UL recognition]	3.0 mm	Class	UL 94	5VA
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	3.2
	Relative permittivity	1 MHz	-	IEC 60250	3.1
	Dissipation factor	100 Hz	10-4	IEC 60250	37
	Dissipation factor	1 MHz	10-4	IEC 60250	75
	Volume resistivity		Ohm·m	IEC 60093	1E15
	Surface resistivity		Ohm	IEC 60093	1E17
	Electrical strength	1 mm	kV/mm	IEC 60243-1	35
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	350
Other properties (23 °C)
	Water absorption (saturation value)	Water at 23 °C	%	ISO 62	0.5
	Water absorption (equilibrium value)	23 °C; 50 % r. h.	%	ISO 62	0.2
	Density		kg/m3	ISO 1183-1	1190
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	260
	Injection molding-Mold temperature		°C	ISO 294	80
	Injection molding-Injection velocity		mm/s	ISO 294	240