Bayblend FR3021
PC/ABS
锑免费，无溴，氯，阻燃

15％矿物填充阻燃注塑级，增加刚度，拉伸模量= 4800兆帕;维卡/乙120温度= 98°C，UL认可94 V-0级（1.5毫米）;锑 - ，氯和无溴阻燃;灼热丝试验（GWFI）：960℃（2.0毫米）。

[Datasheet Bayblend FR3021]

Property		Test Condition	Unit	Standard	typical Value
Rheological properties
	Melt volume-flow rate	240 °C; 5 kg	cm3/10 min	ISO 1133	13
	Molding shrinkage, parallel	150x105x3 mm; 240 °C / MT 80 °C	%	b.o. ISO 2577	0.3 - 0.5
	Molding shrinkage, normal	150x105x3 mm; 240 °C / MT 80 °C	%	b.o. ISO 2577	0.3 - 0.5
	Melt viscosity	1000 s-1; 260 °C	Pa·s	b.o. ISO 11443-A	165
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	4800
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	65
	Yield strain	50 mm/min	%	ISO 527-1,-2	3.0
	Stress at break	50 mm/min	MPa	ISO 527-1,-2	40
	Strain at break	50 mm/min	%	b.o. ISO 527-1,-2	10
	Izod notched impact strength	23 °C	kJ/m2	ISO 180-A	6.0
Thermal properties
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	85
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	92
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	96
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	98
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.46
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.63
	Burning behavior UL 94 (1.5 mm) [UL recognition]	1.5 mm	Class	UL 94	V-0
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	3.1
	Relative permittivity	1 MHz	-	IEC 60250	3.0
	Dissipation factor	100 Hz	10-4	IEC 60250	50
	Dissipation factor	1 MHz	10-4	IEC 60250	70
	Volume resistivity		Ohm·m	IEC 60093	1E14
	Surface resistivity		Ohm	IEC 60093	1E16
	Electrical strength	1 mm	kV/mm	IEC 60243-1	35
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	275
Other properties (23 °C)
	Water absorption (saturation value)	Water at 23 °C	%	ISO 62	0.5
	Water absorption (equilibrium value)	23 °C; 50 % r. h.	%	ISO 62	0.2
	Density		kg/m3	ISO 1183-1	1280
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	240
	Injection molding-Mold temperature		°C	ISO 294	80
	Injection molding-Injection velocity		mm/s	ISO 294	240