Bayblend FR3020
PC/ABS

混合5％矿物填充阻燃;薄壁应用;注塑成型;维卡/乙120 =  103°C; HDT / A> = 85°C，在小壁的厚度很好的UL认证（V-0在0.75毫米）;锑，氯和溴的阻燃剂。

[Datasheet Bayblend FR3020]

Property Test Condition Unit Standard typical Value
Rheological properties
campus image Melt volume-flow rate 240 °C; 5 kg cm3/10 min ISO 1133 20
  Molding shrinkage, parallel 150x105x3 mm; 240 °C / MT 80 °C % b.o. ISO 2577 0.4 - 0.6
  Molding shrinkage, normal 150x105x3 mm; 240 °C / MT 80 °C % b.o. ISO 2577 0.4 - 0.6
  Melt viscosity 1000 s-1; 260 °C Pa·s b.o. ISO 11443-A 200
Mechanical properties (23 °C/50 % r. h.)
campus image Tensile modulus 1 mm/min MPa ISO 527-1,-2 3200
campus image Yield stress 50 mm/min MPa ISO 527-1,-2 65
campus image Yield strain 50 mm/min % ISO 527-1,-2 4.0
  Stress at break 50 mm/min MPa ISO 527-1,-2 50
  Strain at break 50 mm/min % b.o. ISO 527-1,-2 > 30
  Izod notched impact strength 23 °C kJ/m2 ISO 180-A 11
Thermal properties
campus image Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 85
campus image Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 95
campus image Vicat softening temperature 50 N; 50 °C/h °C ISO 306 101
  Vicat softening temperature 50 N; 120 °C/h °C ISO 306 103
campus image Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.7
campus image Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.7
campus image Burning behavior UL 94 [UL recognition] 0.75 mm Class UL 94 V-0
campus image Burning behavior UL 94-5V [UL recognition] 2.0 mm Class UL 94 5VB
  Burning behavior UL 94-5V [UL recognition] 3.0 mm Class UL 94 5VA
Electrical properties (23 °C/50 % r. h.)
campus image Relative permittivity 100 Hz - IEC 60250 3.1
campus image Relative permittivity 1 MHz - IEC 60250 3.0
campus image Dissipation factor 100 Hz 10-4 IEC 60250 50
campus image Dissipation factor 1 MHz 10-4 IEC 60250 70
campus image Volume resistivity   Ohm·m IEC 60093 1E14
campus image Surface resistivity   Ohm IEC 60093 1E16
campus image Electrical strength 1 mm kV/mm IEC 60243-1 35
campus image Comparative tracking index CTI Solution A Rating IEC 60112 275
Other properties (23 °C)
campus image Water absorption (saturation value) Water at 23 °C % ISO 62 0.5
campus image Water absorption (equilibrium value) 23 °C; 50 % r. h. % ISO 62 0.2
campus image Density   kg/m3 ISO 1183-1 1200
Processing conditions for test specimens
campus image Injection molding-Melt temperature   °C ISO 294 240
campus image Injection molding-Mold temperature   °C ISO 294 80
campus image Injection molding-Injection velocity   mm/s ISO 294 240