Bayblend FR3010
PC/ABS
锑免费，无溴，氯，阻燃

注塑级，提高耐热性，维卡/乙120温度= 110°C;  UL认证94 V-0（1.5毫米）;锑，氯和溴阻燃灼热丝试验（GWFI）：960℃（2.0毫米），改进的耐化学性和应力开裂行为;继任者FR2010

[Datasheet Bayblend FR3010 HF]

Property		Test Condition	Unit	Standard	typical Value
Rheological properties
	Spiral flow length	260 °C/80°C; 2 x 8 mm	mm	Bayer test	400
	Melt volume-flow rate	240 °C; 5 kg	cm3/10 min	ISO 1133	25
	Molding shrinkage, parallel	150x105x3 mm; 240 °C / MT 80 °C	%	b.o. ISO 2577	0.5 - 0.7
	Molding shrinkage, normal	150x105x3 mm; 240 °C / MT 80 °C	%	b.o. ISO 2577	0.5 - 0.7
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	2700
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	60
	Yield strain	50 mm/min	%	ISO 527-1,-2	4
	Stress at break	50 mm/min	MPa	ISO 527-1,-2	50
	Strain at break	50 mm/min	%	b.o. ISO 527-1,-2	> 50
	Izod impact strength	23 °C	kJ/m2	ISO 180-U	N
	Izod notched impact strength	23 °C	kJ/m2	ISO 180-A	35
	Izod notched impact strength	-30 °C	kJ/m2	ISO 180-A	10
Thermal properties
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	90
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	100
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	106
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	108
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.76
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.8
	Burning behavior UL 94 (1.5 mm) [UL recognition]	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V [UL recognition]	2.2 mm	Class	UL 94	5VB
	Burning behavior UL 94-5V [UL recognition]	3.0 mm	Class	UL 94	5VA
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	3.2
	Relative permittivity	1 MHz	-	IEC 60250	3.1
	Dissipation factor	100 Hz	10-4	IEC 60250	40
	Dissipation factor	1 MHz	10-4	IEC 60250	70
	Volume resistivity		Ohm·m	IEC 60093	1E14
	Surface resistivity		Ohm	IEC 60093	1E16
	Electrical strength	1 mm	kV/mm	IEC 60243-1	35
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	350
Other properties (23 °C)
	Water absorption (saturation value)	Water at 23 °C	%	ISO 62	0.5
	Water absorption (equilibrium value)	23 °C; 50 % r. h.	%	ISO 62	0.2
	Density		kg/m3	ISO 1183-1	1180
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	240
	Injection molding-Mold temperature		°C	ISO 294	80
	Injection molding-Injection velocity		mm/s	ISO 294	240

Disclaimer