Lead glass can be used to make anti radiation glass, optical glass, electric vacuum glass, low temperature sealing glass, low melting glass, delay line glass, high refractive micro bead glass and artistic container glass, etc.. But if we want to keep the lead glass in good service, its regular maintenance is extremely important. Next, let's introduce the maintenance of lead glass.

　　1、安装时禁止使用潮湿木材质制作窗框，因其收缩，损坏玻璃。

　　1. When installing, forbid to use damp wood material to make WINOOW frame, because of its contraction, damage glass.

　　2、铅玻璃表面不得与硬或粗糙的东西碰擦以免产生伤痕。

　　2, lead glass surface must not touch with hard or rough thing, lest produce scar.

　　3、铅玻璃的使用、贮存环境，应通风干爽，在常温下湿度不应过大。且由于含有丰富的铅和钡,铅玻璃易受酸碱的污染,不易于安装或存放在酸气或潮湿的环境中。

　　3, lead glass use, storage environment, should be ventilated and dry, at room temperature, humidity should not be too large. Because of its rich lead and barium, lead glass is susceptible to acid and alkali pollution and is not easy to install or store in acid, gas or humid environments.

　　4、铅玻璃表面，因保护不当，发生轻微的霉斑，可用无水酒精脱脂棉球抹擦即可除掉。

　　4, lead glass surface, because of improper protection, slight mildew, available anhydrous alcohol cotton ball wipe can be removed.

　　5、铅玻璃是脆性材料，比率较大移置时必须轻拿轻放;装置时必须将窗四处用铅板或者铅橡胶密封，以防四处散漏射线。

　　5, lead glass is a brittle material, the larger rate of displacement must be handled with care; when the device must be around the WINOOW using lead or lead rubber seal, to prevent the spread of leakage ray.

 　　涂料在使用过程中多多少少都活造成一定的损耗，根据施工细节的不同，损耗的差距就会显现出来，那么射线防护涂料的损耗主要是体现在哪些方面呢？

　　1、涂膜损耗
　　涂膜分布造成的射线防护涂料损耗-最大影响因素。一方面，要求漆膜厚度完全均匀是不可能达到的，按照90-10或80-20漆膜厚度控制原则来验收干膜厚度，平均干膜厚度通常会超出设计的干膜厚度，这将引起多消耗涂料，另一方面，在一些施工难度大的部位，过量涂装（超厚）更是不可避免，这也将加大涂料的消耗量。由于涂料分布造成的损耗，辊刷通常在5%-15%，喷涂通常在15%-40%。
 射线防护涂料
　　2、施工损耗
　　与施工方式、构件形状等相关，比如喷涂时的漆雾飞散、过喷等，无气喷涂施工时此项一般在 5%-60%不等。大面积结构比小杆件的损耗小，大风时室外施工也会加大这部分损耗。
　　3、涂料浪费
　　涂料浪费包括：包装桶残留、涂漆设备上的粘附（如泵内与管路损失，辊子和刷子的残留等）、配料不当造成的损失。这部分可以按3%-10%考虑。

如何判断一块铅玻璃质量标准的好坏？
1、铅玻璃外观检查,没有气泡,凝聚物;
2、铅玻璃颜色基本透明,无黑色杂质,色泽统一均匀;